Kimya PETG-S is a 3D printing filament made from PETG (Polyethylene Terephthalate Glycol). It is a durable, flexible polyester that offers a good balance between strength and flexibility, and it also allows for prints with higher clarity or translucency. Thanks to its low cost, PETG is an economical choice for a wide range of applications.
• Good Chemical Resistance.
• Low Moisture Absorbtion.
• Excellent Layer Adhesion.
| Properties | Values | Test Methods |
| Diameter | 1.75 ± 0.1 mm
2.85 ± 0.1 mm
| INS-6712 |
| Density | 1.278 g/cm³ | ISO 1183-1 |
| Moisture Rate | < 1 % | INS-6711 |
| Melt flow index (MFI) | 12.1 g/10min | ISO 1133-1 (@225°C-2.16kg) |
| Glass transition temperature (Tg) | 80°C (176°F) | ISO 11357-1 DSC (10°C/min-20-300°C) |
| Properties | XY | ZX | Test Methods |
| Tensile Modulus | 2,158 MPa (313.0 ksi) | 2,057.5 MPa (298.4 ksi) | ISO 527-2/1A/50 |
| Tensile Strength | 52.2 MPa (7.6 ksi) | 39.3 MPa (5.7ksi) | ISO 527-2/1A/50 |
| Tensile Strain at Strength | 3.4 % | 2.3 % | ISO 527-2/1A/50 |
| Tensile Stress at Break | 52.2 MPa (7.6 ksi) | 39.3 MPa (5.7ksi) | ISO 527-2/1A/50 |
| Tensile Strain at Break (type A) | 3.4 % | 2.3 % | ISO 527-2/1A/50 |
| Flexural Modulus | 1,850 MPa (268.3 ksi) | 1,636 MPa (237.3 ksi) | ISO 178 |
| Deformation at Flexural Strain | 0 % | 4.4 % | ISO 178 |
| Flexural Strength* | 0 MPa (0 ksi) | 63.9 MPa (9.3 ksi) | ISO 178 |
| Flexural Stress at Conventional Deflection (3.5% Strain)* | 69.7 MPa (10.1 ksi) | 58.9 MPa (8.5 ksi) | ISO 178 |
| Flexural Stress at Break | 0 MPa (0 ksi) | 63.9 MPa (9.3 ksi) | ISO 178 |
| Deformation at Flexural Strength | 0 % | 4.5 % | ISO 178 |
| Charpy Impact Resistance | 3.991 kJ/m² (1.9 ft-lbs/in²) | 1.4 kJ/m² (0.7 ft-lbs/in²) | ISO 179-1/1eA |
| Shore Hardness | 76.6 D | 74.1 D | ISO 868 |
| Printing Direction | XY |
| Printing Speed | Initial layers: 10-20 mm/s, further layers 30-60 mm/s |
| Nozzle Temperature | 230°C - 260°C (446°F - 500°F) |
| Bed Temperature | 75°C - 85°C (167°F - 185°F) |
• *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
• The data should be considered as indicative values - Properties can be influenced by production conditions.
Last updated : 2025-10-13
As the conditions or methods of use, including storage, are beyond our control, Airtech International, Inc. does not assume responsibility for the performance of this material for any particular use. The material is sold "as is". Airtech International, Inc. disclaims, and buyer waives, any and all implied warranties, including without limitation the implied warranties of merchantability and of fitness for particular use. The information contained herein represents typical properties and should not be used for specification purposes. Any translation is provided for your convenience only. The official language is English and the official law is California, USA.