Name | Description | Maximum use temperature | |||||||
---|---|---|---|---|---|---|---|---|---|
Name Release Ply A & Release Ply Super A | DescriptionNon-coated nylon peel ply | Maximum use temperature232°C (450°F) | |||||||
Name | |||||||||
Name Release Ply B | DescriptionNon-coated nylon peel ply with tight weave | Maximum use temperature232°C (450°F) | |||||||
Name | |||||||||
Name Release Ply C | DescriptionNon-coated polyester peel ply | Maximum use temperature204°C (400°F) | |||||||
Name | |||||||||
Name Release Ply F & Release Ply Super F | DescriptionNon-coated polyester peel ply | Maximum use temperature204°C (400°F) | |||||||
Name | |||||||||
Name Release Ply G & Stitch Ply G | DescriptionNon-coated polyester peel ply | Maximum use temperature204°C (400°F) | |||||||
Name | |||||||||
Name Ultra Ply 22 T | DescriptionNon-coated polyester peel ply with good drapability | Maximum use temperature204°C (400°F) | |||||||
Name | |||||||||
Name Superlease Blue | DescriptionCoated nylon peel ply | Maximum use temperature232°C (450°F) | |||||||
Name | |||||||||
Name Bleeder Lease® A & Bleeder Lease® B | DescriptionCoated nylon peel ply | Maximum use temperature232°C (450°F) | |||||||
Name | |||||||||
Name Bleeder Lease® C & Bleeder Lease® E | DescriptionCoated fibreglass peel ply | Maximum use temperature427°C (800°F) | |||||||
Name | |||||||||
Name Bleeder Lease® G | DescriptionCoated polyester peel ply | Maximum use temperature204°C (400°F) | |||||||
Name | |||||||||
Name Stik-Ply® ES | DescriptionNylon peel ply with continuous adhesive coating | Maximum use temperature190°C (375°F) | |||||||
Name | |||||||||
Name Stik-Ply® P90P | DescriptionSelf Adhesive porous peel ply | Maximum use temperature190°C (375°F) | |||||||
Name | |||||||||
Name Econolease | DescriptionCoated nylon peel ply | Maximum use temperature204°C (400°F) | |||||||
Name | |||||||||
Name Econoply E & Econoply J | DescriptionNon-coated polyester peel ply | Maximum use temperature121°C (250°F) to 149°C (300°F) | |||||||
Name | |||||||||
Name Econostitch® & Econostitch® G | DescriptionNon-coated peel ply with tracers | Maximum use temperature190°C (375°F) | |||||||
Name | |||||||||
Name Release Ease® 234 TFP, 234 TFP-HP & 234 TFP-1 | DescriptionPorous PTFE coated fibreglass fabrics | Maximum use temperature288°C (550°F) | |||||||
Name | |||||||||
Name Release Ease®234 TFNP & Release Ease®236 TFNP | DescriptionNon-porous PTFE coated fibreglass fabrics | Maximum use temperature288°C (550°F) | |||||||
Name | |||||||||
Name Dahltexx® SP-2 & Dahltexx® SP-3 | DescriptionAir permeable resin barrier material | Maximum use temperature177°C (350°F) to 190°C (375°F) | |||||||
Name | |||||||||
Name Bagside and toolside breathing | Description- | Maximum use temperature- | |||||||
Name |
A Peel Ply is a fabric layer applied on the surface of a composite laminate that can be removed once the composite has cured, leaving a textured surface on the laminate's surface. This is excellent preparation for parts that are to be bonded or painted subsequently.
Release Fabrics are PTFE coated fiberglass fabrics that enable good release in all regularly used resin systems. Non-porous release textiles will easily release from cured laminates and leave a high gloss smooth finish. Porous products allow excess resin, volatiles, and trapped air to escape into the breather during cure, resulting in a textured surface.
Airtech provides the most comprehensive selection of peel plies and release fabrics for multiple layup techniques at different temperatures, available in a variety of widths and at the most competitive prices. The selection of peel ply is determined by how easily a peel ply will release from a surface, which can be used for a unique layup process, which may be best for secondary bonding, what is the material's temperature range, durability, porosity, and general ease of use.
Release fabrics, also known as peel plies, are widely used in the composites industry to achieve consistent surface finishes and bondable surfaces. Airtech offers a large range of peel plies and release fabrics for multiple processes at different temperatures, supplied in different weaves and weights.
Our Release Fabrics/Peel Plies are suitable for use in different resin system temperatures.The useof Release fabrics/peel plies leaves a clean surfaceready for painting and, in most cases, bonding. Customers can select Nylon or Polyester peel plies, either uncoated or silicone-coated for easy release.